ASTM A182 WP317 Stainless Steel Socket weld fittings, SS 317 Tee, wp317 Elbow SS 317 Union Manufacturer & Suppliers In India
Manufacturer, Supplier and Exporter of ASTM A182 WP317 Stainless Steel Socket weld fittings in India
- ASTM A182 WP317 Stainless Steel Socket weld fittings
- ASTM A182 WP317 Stainless Steel Socket weld fittings dimensional range & specification
- ASTM A182 WP317 Stainless Steel Socket weld fittings sizes & stock
- ASTM A182 WP317 Stainless Steel Socket weld fittings price
- ASTM A182 WP317 Stainless Steel Socket weld fittings manufacturing process
- ASTM A182 WP317 Stainless Steel Socket weld fittings useful info
- ASTM A182 WP317 Stainless Steel Socket weld fittings other brand manufacturers
Since 2004, Ashtapad Overseas has manufactured ASTM A182 WP317 Stainless Steel Socket weld fittings, flange, elbow, tee, reduction, caps, forged fitting materials for oil and natural gas pipelines, refinery and petro chemistry facilities, nuclear power and electricity production plants, refinement and extrication plants, dams and hydroelectric power plants and shipbuilding industry. Ashtapad Overseas is a largest manufacturer, supplier & exporter of pipe fitting pieces and fabrication since the company’s superior technology in world standards and quality.
Ashtapad Overseas is among the leading companies in the sector of manufacturing ASTM A182 WP317 Stainless Steel Socket weld fittings, pipe fittings & flanges with its superior technology in compatible with the world standards, and has been the choice of many professionals and companies. Ashtapad has a capacity of fulfilling all the demands of the sector through the manufacture of carbon steel, stainless steel, alloy steel and specific steel groups.
We offer wide gamut of ASTM A182 WP317 Stainless Steel Socket weld fittings that are widely used in diverse industries. Fittings and flanges of SS 304 / 304L are made available on request of the customers. Can be made available in forms of Reducers – Concentric / Eccentric, Elbows, Tees, Caps, Stub Ends, Flanges, Fasteners, etc Our gamut of products conform various standards such as the varied grades of stainless steel butt weld fittings that we supply are.
Standard: ASTM / ASME A/SA 403 GR WP "S" / "W" / " WX"
Grade: 304, 304L, 304H, 309S, 309H, 310S, 310H, 316, 316TI, 316H, 316L, 316LN, 317, 317L, 321, 321H, 347, 347H, 904L. .
Origin: West Europe / Japan / Indian / USA / Korean
ASTM A182 WP317 Stainless Steel Socket weld fittings Production Range
|Specification||ASTM A182 & ASME SA182|
|Type||Seamless / Welded / Fabricated|
|Bending Radius||R=1D, 2D, 3D, 5D, 6D, 8D, 10D or Custom|
|Range||½”NB to 48”NB in Sch 10s, 40s, 80s, 160s, XXS.|
|Dimensions||ANSI/ASME B16.9, B16.28, MSS-SP-43.|
Test Certificates: Manufacturer Test Certificate as per EN 10204 / 3.1B, Raw Materials Certificate, 100% Radiography Test Report, Third Party Inspection Report
High Pressure Forged Pipe Fittings / Threaded and Socket Weld Pipe Fittings
|ASTM A182 WP317 stainless steel 90° Elbows||ASTM A182 WP317 stainless steel Couplings||
Sizes 1/8" – 4"
Pressure Ratings –
|ASTM A182 WP317 stainless steel 45° Elbows||ASTM A182 WP317 stainless steel Reducers|
|ASTM A182 WP317 stainless steel Street Elbows||ASTM A182 WP317 stainless steel Inserts|
|ASTM A182 WP317 stainless steel Tees||ASTM A182 WP317 stainless steel Caps|
|ASTM A182 WP317 stainless steel Crosses||ASTM A182 WP317 stainless steel Unions|
We are specialized in:
- Flanges according to ASTM A182 Grade F304, F304L F316L
- Pipes according to ASTM A312 Grade TP304, TP304L, TP3016L
- Fittings according to ASTM A403 Grade WP304, WP304L, WP316L
|Stainless Steel||Tradename||UNS no.||Werkstoff No.|
Key Properties of ASTM A182 WP317 Stainless Steel Socket weld fittings
- High corrosion resistance in tough environments
- Lower intergranular precipitation
- High resistance to pitting and crevice corrosion
Common Applications ASTM A182 WP317 Stainless Steel Socket weld fittings
- Pulp and paper manufacturing plants
- Chemical processing equipment
- Petrochemical processing equipment
- Textile machinery and equipment
- Vessels and tanks
317L is an molybdenum-bearing austenitic stainless steel, with greatly increased resistance to chemical attack as composed to the conventional chromium-nickel austenitic steel tubes as 304L & 316L. the addition of molybdenum gives alloy 317L tubing improved resistance to chloride and other halides. Due to its low carbon content the 317L tubing can be welded without risk of sanitization due to inter granular corrosion that can result from chromium carbide precipitation in the grain boundaries. 317L is non magnetic in the annealed condition, but may become slightly magnetic as result of welding.
|Technical composition (%)||Fe||Cr||Ni||Mo||Mn||Si||P||C||S|
|Tensile strenght (mpa, min)||515 – 750|
|Yield strength (0.2% offset mpa, min)||205|
|Elongation (%, min)||35|
|Density / weight (g / cm3 / kg)||7.90|
High molybdenum and nitrogen contents can significantly improve pitting resistance as illustrated in the preceding table of Pitting Resistance Equivalents (PRE). The PRE is based on the results of corrosion tests in which it was found that nitrogen was 30 times more effective than chromium and approximately 9 times more effective than molybdenum in enhancing chloride pitting resistance.
The temperature of the onset of crevice corrosion as determined in a modified AST G-48B test is a useful means of ranking the relative resistance of stainless and nickel-base alloys. The Critical Crevice Corrosion Temperatures table that follows demonstrates that crevice corrosion resistance for austenitic stainless steels increases with the alloyâ€™s molybdenum and nitrogen content.
|Crevice Corrosion in a Simulated
FGD System Environment
Weight Loss (g/cm2)
*72-hour exposure based on ASTM G-48B procedure using the following solution:
7 vol.%H2SO4, 3 vol%HCI, 1 wt% CuCl2, 1 wt%FeCl3
The chromium-nickel-molybdenum steels all have excellent resistance to oxidation and a low rate of scaling in ordinary atmospheres at temperatures up to 1600-1650 °F (871-899 °C).
The physical and mechanical properties of 317LMN and Alloy 317L stainless steels are similar to those of more conventional austenitic stainless steels and can, therefore, be fabricated in a manner similar to Alloys 304 and 316.
Cities We Deliver To: Mumbai, Bengaluru, Chennai, New Delhi, Pimpri-Chinchwad, Houston, Dubai, Seoul, Hyderabad, Singapore, Abu Dhabi, Pune, Kolkata, Gurgaon, Navi Mumbai, Ahmedabad, Tehran, Calgary, Noida, Riyadh, Vadodara, London, Coimbatore, Jakarta, Istanbul, Bangkok, Kuwait City, Thane, Sharjah, Muscat, Edmonton, Busan, Mexico City, Doha, Jeddah, Aberdeen, Cairo, Geoje-si, Perth, Santiago, Chandigarh, Indore, Kuala Lumpur, Rio de Janeiro, Dammam, Melbourne, Madrid, Surat, Bhopal, Ulsan, Faridabad, La Victoria, Bogota, Lahore, Los Angeles, Algiers, Chiyoda, Ankara, Ho Chi Minh City, Toronto, Hong Kong, Rajkot, Brisbane, Petaling Jaya, Ernakulam, Secunderabad, Gimhae-si, Al Jubail, Port-of-Spain, Thiruvananthapuram, Milan, Atyrau, Lagos, Hanoi, Howrah, Sydney, Ahvaz, Karachi, New York, Caracas, Vung Tau, Al Khobar, Manama, Montreal, Granada, Courbevoie, Visakhapatnam, Ludhiana, Moscow, Dallas, Haryana, Colombo, Mumbai, Delhi, Bangalore, Hyderabad, Ahmedabad, Chennai, Kolkata, Surat, Pune, Nagpur, Indore, Thane, Bhopal, Visakhapatnam, Vadodra, Nashik, Faridabad, Rajkot, Aurangabad, Ranchi, Coimbatore, Raipur, Mysore, Bhubaneswar, Salem, Bhilai, Bhiwandi, Bikaner, Mangalore, Kochi (Cochin), Bhavnagar, Tirupur, Ankleshwar, Assam, Siliguri
Countries We Deliver To: India, United States, United Arab Emirates, Canada, Pakistan, Peru, Chile, Spain, France, United Kingdom, Indonesia, Israel, Iran, Kuwait, Mexico, Malaysia, Nigeria, Serbia, Singapore, Taiwan, Chile, Venezuela, Ecuador, Saudi Arabia, Netherlands, Brazil, Colombia, Ghana, Iran, Denmark, Poland, Australia, Afghanistan, Bahrain, Costa Rica, Egypt, Iraq, Jordan, South Korea, Kazakhstan, Sri Lanka, Lithuania, Norway, Oman, Philippines, Poland, Qatar, Russia, Vietnam, South Africa, Nigeria, Mexico, Turkey, Hungary, Algeria, Angola, Argentina, Austria, Azerbaijan, Bangladesh, Belarus, Belgium, Bhutan, Bolivia, Bulgaria, Croatia, Czech Republic, Estonia, Finland, Greece, Italy, Japan, Libya, Romania, Thailand, Trinidad & Tobago,Tunisia, Ukraine, Yemen, Hong Kong, Gabon, China, Portugal, Switzerland, New Zealand, Sweden, Slovakia, Kenya, Lebanon, Morocco, Mongolia
Europe: Germany, Netherlands, Russia Finland, Czech, Ukraine, Italy, Spain, Poland
Middle East:Iran, UAE, SA, Iraq, Qatar, Isreal, Jordan, Bahrain, Kuwait
South America:Brazil, Chile, Peru, Venezuela, Uruguay, Argentina
Africa: Egypt, South Africa, Nigeria
Central & North America:Mexico, US, Canada, Costa Rica
South East Asia and Pacific:Japan, South Korea, Singapore, Thailand, Indonesia, Australia
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Erne Fittings, Austria
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Metalfar, Italy
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Lame S.r.l., Italy
- ASTM A182 WP317 Stainless Steel Socket weld fittings | BKL- Thai Benkan, Thailand
- ASTM A182 WP317 Stainless Steel Socket weld fittings | BENKAN Corporation, Japan
- ASTM A182 WP317 Stainless Steel Socket weld fittings | TecnoForge, Italy
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Ulma, Spain
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Mega, Italy
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Melesi, Italy
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Interfit, France
- ASTM A182 WP317 Stainless Steel Socket weld fittings | Raccortubi S.p.A., Italy